Bronze Bra9zh3l (Brazh9-4L)

Designation

Name The value
Designation GOST Cyrillic БрА9Ж3Л
Designation GOST Latin BpA9Zh3L
Transliteration BrA9G3L
By chemical elements BaAl9Fe3
Name The value
Designation GOST Cyrillic БрАЖ9-4Л
Designation GOST Latin BpAZh9-4L
Transliteration BrAG9-4L
By chemical elements BaAlFe9-4

Description

Bronze Bra9zh3l used: for the manufacture of anti-friction casting parts; valve parts; casting parts mining and metallurgical machinery; casting parts, metallurgical engineering (simple shaped castings, valves (except steam), gears, gear wheels, boxes and plates, valves, bearings, bushings, pump bodies, pressure rings, rods, nuts, seals and other bearing parts used at pressures up to 200 kgf/cm2, paired with steel cemented worm); casting parts for shipbuilding, ship engineering and instrumentation.

Note

Aluminum bronze. Recommended as a substitute for tin bronzes. Anti-corrosion, heat-resistant (up to 265 °C) bronze, resistant to atmosphere, fresh and sea water.
The coefficient of friction of bronze of 0.18 without lubrication with grease of 0.004. The maximum allowable speed — 10 m/s Maximum load rating: static — 300 kgf/cm2, the dynamic — 600 kgf/cm2 s.

Standards

Name Code Standards
Castings with special properties (iron and steel) В83 KSt 81-033:2009
Non-ferrous metals, including rare, and their alloys В51 GOST 493-79, OST 4.021.009-92, OST 4.021.011-92, STP М314-95
Castings, non-ferrous metals and alloys В84 OST 1 90046-72, OST 24.916.01-71, OST 5Р.9209-82

Chemical composition

Standard P Mn Si Ni Fe Cu As Al Zn Sn Sb Pb
KSt 81-033:2009 ≤0.1 ≤0.5 ≤0.2 ≤1 2-4 Rest - 8-10.5 ≤1 ≤0.2 ≤0.05 ≤0.1
OST 5Р.9209-82 ≤0.1 ≤0.5 ≤0.2 ≤1 2-4 Rest ≤0.05 8-10.5 ≤1 ≤0.2 ≤0.05 ≤0.1
OST 24.916.01-71 ≤0.1 ≤0.5 ≤0.2 ≤1 2-4 Rest ≤0.05 8-10 ≤1 ≤0.2 ≤0.05 ≤0.1
Cu is the basis.
According to GOST 493-79, OST 24.916.01-71, OST 5P.9209-82 and STP M314-95, the total content of impurities is ≤ 2.70%. Impurities, which are not regulated, are included in the total amount of impurities.
According to OST 24.916.01-71 lead content is allowed up to 0.30% when used for shaped casting, with the total amount of impurities allowed to be ≤ 1.00%.

Mechanical properties

sT|s0,2, MPa σU, MPa d5, % KCU, kJ/m2 HB, MPa
Castings are supplied without heat treatment
≥196 ≥392 ≥10 ≥196 ≥100
≥196 ≥490 ≥12 ≥196 ≥100
- ≥392 ≥10 - ≥100

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d5 Elongation after rupture
KCU Toughness
HB Brinell hardness number

Physical characteristics

Temperature r, kg/m3
20 7500

A description of the physical symbols

Name Description
r Density
l Coefficient of thermal conductivity
R UD. the resistivity