Designation
| Name |
The value |
| Designation GOST Cyrillic |
ВД17 |
| Designation GOST Latin |
BD17 |
| Transliteration |
VD17 |
| By chemical elements |
ВД17 |
| Name |
The value |
| Designation GOST Cyrillic |
1170 |
| Designation GOST Latin |
1170 |
| Transliteration |
1170 |
| By chemical elements |
1170 |
Description
Alloy ВД17 used: for the manufacture of compressor blades of the engines working at temperatures up to +250 °C; for the production of profiles with cross-sectional area of 200 cm2 and a diameter of circumcircle up to 350mm suitable for use in the aviation industry and special machine building industries.
Standards
| Name |
Code |
Standards |
| Bars and shapes |
В52 |
GOST 13616-97, GOST 13617-97, GOST 13618-97, GOST 13619-97, GOST 13620-90, GOST 13621-90, GOST 13622-91, GOST 13623-90, GOST 13624-90, GOST 13737-90, GOST 13738-91, GOST 17575-90, GOST 17576-97, GOST 29296-92, GOST 29303-92, GOST Р 50066-92, GOST Р 50067-92, GOST Р 50077-92, OST 1 92093-83, OST 1 90113-86 |
| Sheets and strips |
В53 |
OST 1 90009-76 |
| Non-ferrous metals, including rare, and their alloys |
В51 |
OST 1 90048-90 |
| Processing of metals by pressure. Forgings |
В03 |
OST 1 90073-85 |
| Bars |
В55 |
OST 1 90395-91 |
Chemical composition
| Standard |
Mn |
Si |
Fe |
Cu |
Al |
Ti |
Zn |
Mg |
| OST 1 90048-90 |
0.45-0.7 |
≤0.3 |
≤0.3 |
2.6-3.2 |
Rest |
≤0.1 |
≤0.1 |
2-2.4 |
Al is the base.
According to GOST 4784-97 and OST 1 90048-90, the mass fraction of each other impurity (not regulated) ≤ 0.05%, the total mass fraction of other impurities ≤ 0.10%.
Mechanical properties
| Section, mm |
sT|s0,2, MPa |
σU, MPa |
d5, % |
| Forgings supplied. Quenching + aging |
| - |
≥260 |
≥400 |
≥10 |
| Forgings section up to 100 mm OST 1 90073-85. Mode T1: Quenching + artificial aging (indicated by the direction of samples) |
|
≥255 |
≥390 |
≥10 |
|
≥255 |
≥375 |
≥10 |
| Extruded normal strength with the cross-sectional area 200 cm2 and a diameter of the circumscribed circle of up to 350 mm. (sample longitudinal cross-section shows the thickness of the shelf). Quenching + artificial aging |
|
≥275 |
≥430 |
≥10 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d5 |
Elongation after rupture |
Physical characteristics
| Temperature |
Е, HPa |
r, kg/m3 |
R, Mr. · m |
| 20 |
72 |
2750 |
55 |
A description of the physical symbols
| Name |
Description |
| Е |
The normal elasticity modulus |
| r |
Density |
| l |
Coefficient of thermal conductivity |
| R |
UD. the resistivity |