Steel 05Х18АН5ФЛ

Designation

Name The value
Designation GOST Cyrillic 05Х18АН5ФЛ
Designation GOST Latin 05X18AH5FL
Transliteration 05H18AN5FL
By chemical elements 05Cr18NН5V

Description

05Х18АН5ФЛ steel is used: for the manufacture of the 1st, 2nd and 3rd groups casting parts of valves and actuators to it, not subjected to welding, surfacing and operating in aggressive environments at temperatures of the working medium from -100 to +300 °C without limitation of the rated working pressure.

Note

Steel 05Х18АН5ФЛ is a substitute for steel 12H18N9TL.

Standards

Name Code Standards
Steel castings В82 OST 26-07-402-83, ST ЦКБА 014-2004

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu N V Ce
ST ЦКБА 014-2004 ≤0.07 ≤0.03 ≤0.03 1-2 17.5-20 0.2-1 5.5-6.5 Rest ≤0.3 0.12-0.16 0.1-0.3 ≤0.02
Fe is the basis.
According to CT CKBA 014-2004, a carbon content of up to 0.10% is allowed in the absence of test requirements for resistance to intergranular corrosion. When steel is smelted in electric furnaces with acid lining, the mass fraction of silicon is allowed up to 2.00% in the absence of the requirements for resistance to intergranular corrosion.

Mechanical properties

sT|s0,2, MPa σU, MPa d y, % KCU, kJ/m2
Casting parts of pipe fittings. Heated to 1100-1150 °C (extract 2-3 h), cooling in water KCU+20/-196
≥250 ≥500 ≥25 ≥34 ≥1500/600

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d Elongation after rupture
y The relative narrowing
KCU Toughness