Steel 05KH18N10T (0Х18Н10Т)
|Designation GOST Cyrillic||05Х18Н10Т|
|Designation GOST Latin||05X18H10T|
|By chemical elements||05Cr18Н10Ti|
|Designation GOST Cyrillic||0Х18Н10Т|
|Designation GOST Latin||0X18H10T|
|By chemical elements||0Cr18Н10Ti|
05KH18N10T steel is used: for the manufacture of thin-sheet cold-rolled steel; bellows-expansion joints.
Steel corrosion and heat-resistant austenitic class.
Steel 05KH18N10T has a high ability to deep drawing than steel grades 08KH18N10T and 12KH18N10T.
|Classification, nomenclature and General rules||В30||GOST 5632-72|
|Blanks. Of the workpiece. Slabs||В31||OST 3-1686-90, TU 14-1-4681-89|
|Tape||В34||OST 5.9093-72, TU 14-1-4606-89|
|Sheets and strips||В33||TU 14-105-451-86, TU 14-1-3874-84|
|Bars and shapes||В32||TU 14-11-245-88|
According to GOST 5632-72, TU 14-1-3874-84 and TU 14-1-4606-89 the content of Ti% = 5С% - 0,6%.
According to TU 14-1-3874-84, according to the agreement between the consumer and the supplier, the steel is treated with synthetic slag (it is introduced by calculation of silicocalcals and cerium (misch metal) in an amount of 0.05-0.20% and 0.01-0.10% respectively, which chemical analysis is not determined). The residual content of aluminum in steel is not more than 0.10%. The ratio of chromium to nickel is not more than 1.8. By agreement of the parties, it is allowed to supply thick-gauge steel coils with the requirements for the mass fraction of carbon not more than 0.05%, manganese 1.20-2.00%. The rest of the elements are GOST 5632 for steel 08H18N10T.
|Section, mm||sT|s0,2, MPa||σU, MPa||d4|
|Sheet cold rolled steel in the delivery state on the other 14-1-3874-84 (0.3-1.0 mm), THE 14-1-4606-89 (1.5-1.8 mm). Samples of the cross|
Description mechanical marks
|sT|s0,2||Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%|
|σU||Limit short-term strength|
|d4||Elongation after rupture|