Steel 10Х13Г18Д (DI-61; 12Х13Г18Д)
Designation
Name | The value |
---|---|
Designation GOST Cyrillic | 10Х13Г18Д |
Designation GOST Latin | 10X13G18D |
Transliteration | 10H13G18D |
By chemical elements | 10Cr13Mn18Cu |
Name | The value |
---|---|
Designation GOST Cyrillic | ДИ-61 |
Designation GOST Latin | DI-61 |
Transliteration | DI-61 |
By chemical elements | CuИ-61 |
Name | The value |
---|---|
Designation GOST Cyrillic | 12Х13Г18Д |
Designation GOST Latin | 12X13G18D |
Transliteration | 12H13G18D |
By chemical elements | 12Cr13Mn18Cu |
Description
10Х13Г18Д steel is used: for the manufacture of welded products of home appliances, cars, consumer goods, machines and devices food and commercial machinery, plate heat exchangers.
Note
Steel heat-resistant austenitic class.
It is recommended to replace the steel grades 12X18H10T, 08H18N10.
The steel has high ductility for deep forming.
Standards
Name | Code | Standards |
---|---|---|
Sheets and strips | В33 | GOST 5582-75, TU 14-1-3848-84, TU 14-1-1995-76 |
Classification, nomenclature and General rules | В30 | GOST 5632-72 |
Blanks. Of the workpiece. Slabs | В31 | OST 3-1686-90 |
Thermal and thermochemical treatment of metals | В04 | STP 26.260.484-2004 |
Welding and cutting metals. Soldering, riveting | В05 | TU 14-1-4823-90 |
Bars and shapes | В32 | TU 14-131-796-89, TU 14-11-245-88, TU 14-131-759-88, TU 14-1-1995-77 |
Chemical composition
Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | V | Ti | Mo | W |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
GOST 5632-72 | 0.07-0.12 | ≤0.025 | ≤0.03 | 17.5-19.5 | 12-14 | ≤0.8 | ≤2 | Rest | 0.8-1.2 | ≤0.2 | ≤0.2 | ≤0.3 | ≤0.2 |
Fe is the basis.
According to GOST 5632-72 the chemical composition is given for steel 10Х13Г18Д.
According to GOST 5632-72 the chemical composition is given for steel 10Х13Г18Д.
Mechanical properties
Section, mm | sT|s0,2, MPa | σU, MPa | d5, % |
---|---|---|---|
Bars hot rolled and forged at STP 26.260.484-2004. Quenching in water or air with 1030-1070 °C | |||
≥320 | ≥630 | ≥45 |
Description mechanical marks
Name | Description |
---|---|
sT|s0,2 | Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
σU | Limit short-term strength |
d5 | Elongation after rupture |
Technological properties
Name | The value |
---|---|
Features of heat treatment | Steel products for equipment of chemical industry termoobrabotannyj according to mode: heating to 1050±20 °C, the holding time at the heating for hardening to products with a wall thickness up to 10 mm - 30 min, over 10 mm - 20 min + 1 min per 1 mm max thickness cooling products with wall thickness up to 10 mm in the air, over 10 mm in water. |