Steel 16ГДНМЛ

Designation

Name The value
Designation GOST Cyrillic 16ГДНМЛ
Designation GOST Latin 16GDHML
Transliteration 16GDNML
By chemical elements 16MnCuНMo

Description

16ГДНМЛ steel is used: for the manufacture of shaped castings of complex shape responsible different loaded parts shipbuilding with wall thickness up to 130 mm; the component elements of the anchor chains (swivels, shackles), operated in sea water under the influence of significant static and cyclic loads; parts operating at low temperatures.

Note

Dispersion-hardening steel of pearlitic class.

Standards

Name Code Standards
Steel castings В82 OST 5Р.9285-95

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu Mo
OST 5Р.9285-95 0.16-0.22 ≤0.035 ≤0.03 1-1.4 ≤0.3 0.5-0.75 0.8-1.2 Rest 0.8-1.2 0.15-0.3
Fe is the basis.
According to OST 5R.9285-95, the content of chromium up to 0.50% and molybdenum up to 0.12% is not a defect sign provided that the requirements of the standard are observed and if there are no special instructions in the technical conditions of the order or drawing.
According to OST 5R.9285-95, in the case of steel smelted in the main electric furnaces as cold-resistant (technical conditions of the order or requirements of the drawing), the sulfur and phosphorus content should not be more than 0.020% of each. As agreed by the manufacturer with the developer OST 5P.9285-95 (CRI "Prometey"), the content of sulfur and phosphorus is allowed up to 0.030% of each.

Mechanical properties

sT|s0,2, MPa σU, MPa d y, % KCU, kJ/m2 HB, MPa
Castings for shipbuilding. Normalization at 950-980 °C + quenching in water from 900-950 °C + vacation at 600-650 °C, cooling in water
≥410 ≥690 ≥17 ≥40 ≥600 190-240

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d Elongation after rupture
y The relative narrowing
KCU Toughness
HB Brinell hardness number

Technological properties

Name The value
Weldability welded without any restrictions. The welding process - SMAW. With a significant amount of welding it is recommended that subsequent vacation.