Steel 31KH19N9MVBTL (ЭИ572Л; 30Х19НМВБТЛ)

Designation

Name The value
Designation GOST Cyrillic 31Х19Н9МВБТЛ
Designation GOST Latin 31X19H9MBBTL
Transliteration 31H19N9MVBTL
By chemical elements 31Cr19Н9MoWNbTi
Name The value
Designation GOST Cyrillic ЭИ572Л
Designation GOST Latin EI572L
Transliteration EhI572L
By chemical elements -
Name The value
Designation GOST Cyrillic 30Х19НМВБТЛ
Designation GOST Latin 30X19HMBBTL
Transliteration 30H19NMVBTL
By chemical elements 30Cr19НMoWNbTi

Description

31KH19N9MVBTL steel is used: for the manufacture of castings of high-temperature parts (impellers turbines, turbochargers, turbine and guide blades, guide vanes).

Note

Steel heat-resistant austenitic class.

Standards

Name Code Standards
Castings with special properties (iron and steel) В83 GOST 2176-77
Steel castings В82 GOST 977-88, TU 108.02.115-86

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu Ti Mo Nb W
GOST 977-88 0.26-0.35 ≤0.02 ≤0.035 0.8-1.5 18-20 ≤0.8 8-10 Rest - 0.2-0.5 1-1.5 0.2-0.5 1-1.5
GOST 2176-77 0.26-0.35 ≤0.02 ≤0.035 0.8-1.5 18-20 ≤0.8 8-10 Rest ≤0.3 0.2-0.5 1-1.5 0.2-0.5 1-1.5
Fe is the basis.
According to GOST 2176-77 the chemical composition is given for steel grade 31Х19Н9МВБТЛ (ЭИ572Л; 30Х19НМВБТЛ). Deviations from the norms of chemical composition are allowed: for carbon ± 0.020%; for silicon ± 0.10%; on manganese, copper, chromium and nickel ± 0.10% each; by titanium and tungsten ± 0.050% each; by vanadium, molybdenum and niobium ± 0.020% each.

Mechanical properties

Section, mm sT|s0,2, MPa σU, MPa d5, % KCU, kJ/m2
Casting. Quenching in water from 1150-1180 °C + Aging at 700-800 °C, air cooling
100 ≥294 ≥540 ≥12 ≥294

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d5 Elongation after rupture
KCU Toughness