Steel 35ХС2Н3М1ФА (VC-9)

  • Steel 35KhSN3M1A (VKS-8)
  • Steel 30Kh2GSN2VM (30Kh2GSN2M1; VL-1)
  • Steel 30Kh2GSNVM (VL-1D)
  • Steel 30Х2Н2СВМФА (VKS-3)
  • Steel 30KhGSN2A (30KhGSNA)
  • Steel 30KhGSN2MA (30KhGSNMA)
  • Steel 30ХН3М1ФА (30ХН3М1Ф)
  • Steel 30ХН3М2ФА (30ХН3М2Ф)
  • Steel 32KhN8M1FK5A (VKS-6)
  • Steel 34KhMA (34KhM)
  • Steel 34KhN3MA (0KhN3M)
  • Steel 35KhMA (35KhMAR)
  • Steel 35KhN1M2FA
  • Steel 35KHN3MFA (35KHN3MFAR)
  • Steel 35ХС2Н3М1ФА (VKS-9)
  • Steel 28ХНН3МФА (28ХН3МФ)
  • Steel 36KHN3MFA (36KHN3MF)
  • Steel 38Kh3SNMVFA (SP38)
  • 38KhMFYUA steel
  • 38KhN3MFA steel (38KhN3MF)
  • 40GMFR steel
  • Steel 40KhN2SVA (EI643)
  • Steel 40KhN2SMA (EI643M)
  • Steel 42Kh2GSNM (VKS-1)
  • 43Kh3SNMVFA steel (SP43)
  • Steel 45Г15Н9Х2ЮФ (EP769)
  • 45Kh3NM2FA steel
  • Steel АЦ28ХГН2АФБ
  • Steel АЦ28ХГН3ФТ
  • B2G steel
  • X11MNAFB steel
  • 20KhGSNM steel
  • Steel 01N17K12M5T (EP845; VKS-240)
  • Steel 02N18K9M5T (EP637A; VKS-210)
  • Steel 03N18K8M5T (VKS-170; EK21)
  • Steel 03N19K6M5TR (EP631)
  • Steel 03Cr14H7V
  • Steel 08Х15Н25Т2МФР (EP674)
  • Steel 09Х16НМ2Д (EP887; VNS28)
  • Steel 120G13 (EI256)
  • 12Kh3GNMFBA steel
  • Steel 15Х16Н3КАМФ2 (VNS-47; EK81)
  • 15Kh2GMF steel
  • 15Kh2NMFA steel
  • Steel 16X16H3MAD (EP811; VSN21)
  • Alloy 20ХГСН2МФА (DI107)
  • Steel 28Kh3SNMVFA (SP28; EP326A)
  • Steel 25Х12Н2В2М2Ф (EP311; VNS-6)
  • Steel 25Х20Н9В2М (EP466)
  • Steel 25Kh2GNTA
  • Steel 25Х2ГНТРА
  • Steel 25Х2Н4МФА
  • Steel 25Kh2NMF (25Kh2NMFA)
  • Steel 25KhGSNMA
  • Steel 25KhN3MFA (25KhN3MFAR)
  • Steel 25ХСНВФА (VP25)
  • Steel 26ХН3М2ФА (26ХН3М2ФАA)
  • Steel 26KhN3MF (26KhN3MFA)
  • Steel 26KhN4MF (26KhN4MFA)
  • Steel 27ХН3М2ФА (27ХН3М2Ф)
  • Steel 27ХН3МФА (27ХН3МФ)

    • Designation

    Name The value
    Designation GOST Cyrillic 35ХС2Н3М1ФА
    Designation GOST Latin 35XC2H3M1FA
    Transliteration 35HS2N3M1FA
    By chemical elements 35CrС2Н3Mo1V
    Name The value
    Designation GOST Cyrillic ВКС-9
    Designation GOST Latin BKC-9
    Transliteration VKS-9
    By chemical elements WCoС-9

    Description

    35ХС2Н3М1ФА steel is used: for the manufacture of critical heavily loaded parts, aircraft and aerospace industries.

    Note

    Steel high strength high quality.

    Standards

    Name Code Standards
    Classification, nomenclature and General rules В20 OST 1 90005-91
    Blanks. Of the workpiece. Slabs В31 TU 1-92-156-90

    Chemical composition

    Standard C Mn Cr Si Ni Fe V Mo
    30-0.38 0.05-0.5 0.8-1.2 2.1-2.8 2.6-3 Rest 0.05-0.15 0.3-1.2
    Fe is the basis.
    The chemical composition of steel 35ХС2Н3М1ФА (VKS-9) is given under the patent of the Russian Federation No. 1316285 "High-strength structural steel". The steel should contain one element from the group of rare earth metals, including lanthanum and cerium - 0.001-0.05% and not less than one element from the group of alkaline earth metals, including magnesium and calcium, 0.001-0.05%.

    Mechanical properties

    Section, mm sT|s0,2, MPa σU, MPa d5, % y, % KCU, kJ/m2 HRC
    Forgings. Normalization at 890-910 °C, air cooling + Tempering in oil 940-960 °C + Vacation at 200-280 °C (extract 2-3 h), cooling in oil or air
    ≥1570 ≥1910 ≥9 ≥40 ≥490 -
    Gradation of performance properties of the finished heat-treated parts for OST 1 90005-91
    - - 1910-2110 - - - 50.5-53

    Description mechanical marks

    Name Description
    sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
    σU Limit short-term strength
    d5 Elongation after rupture
    y The relative narrowing
    KCU Toughness
    HRC Rockwell hardness (indenter diamond spheroconical)