Steel ПК70Д3-69 (Ж70Д3-69)

Designation

Name The value
Designation GOST Cyrillic ПК70Д3-69
Designation GOST Latin PK70D3-69
Transliteration PK70D3-69
By chemical elements PCo70Cu3-69
Name The value
Designation GOST Cyrillic Ж70Д3-69
Designation GOST Latin Zh70D3-69
Transliteration G70D3-69
By chemical elements Ж70Cu3-69

Description

Steel ПК70Д3−69 is used: for the manufacture by the method of single pressing sredneshirotnykh structural components used in mechanical engineering and instrument making; tool holders of the tool.

Note

Powder steel carbon alloy with copper.
The material should be applied after the impregnation with compounds that protect against internal corrosion. Compositions for the impregnation in accordance with OST 4G 0.054.213.

Standards

Name Code Standards
Hard alloys, ceramic-metal products and metal powder В56 OST 107.460094.118-88, OST 107.460009.002-90

Chemical composition

Standard C Fe Cu
OST 107.460094.118-88 0.5-0.8 Rest 2.5-3
Fe is the basis.

Mechanical properties

Section, mm σU, MPa d KCU, kJ/m2 HB, MPa
Properties of the material to heat treatment at OST 107.460094.118-88
≥392 ≥1 ≥98 140-210

Description mechanical marks

Name Description
σU Limit short-term strength
d Elongation after rupture
KCU Toughness
HB Brinell hardness number

Physical characteristics

Temperature r, kg/m3
20 6700

A description of the physical symbols

Name Description
Е The normal elasticity modulus
l Coefficient of thermal conductivity
С Specific heat

Technological properties

Name The value
Microstructure Pelletieri. Allowed ferrite to 50% and cementite in the form of a torn grid.