|Mark||Analogue||W. Nr.||Aisi Uns||En||Order|
|15Х1М1Ф||1.8521||15crmov5-9||Delivery from the stock, in stock|
Buy steel grades 15H1M1 °F, 15CrMoV5−9, 1.8521 at the best price from the manufacturer, the company offers Electrocentury-steel. Supplier ensures the quality and timely delivery of the metal
Buy sheet, strip and wire of low alloy structural steel 15H1M1 °F, 15CrMoV5−9, 1.8521. the company offers Electrocentury-steel. The provider ensures timely delivery of products to the address specified by the consumer. Subject to the necessary price quality products from manufacturer.
Composition and properties
Boiler Structural steel grade refers to 15H1M1 °F steels boiler group and manufactured domestic steel industry on technical requirements GOST 2590 and TU 14−3R-55−2001. The chemical composition was the following:
|The percentage||0,10…0,16||0,17…0,37||0,40…0,70||1,1…1,4||0,9…1,1||0,20 0,25…||To 0.25|
TU14−3P-55−2001 allows for the presence in the composition of the steel and copper not higher than 0.25%, and also metallurgical impurities — sulfur and phosphorus. The amount of sulfur and phosphorus can not be more than 0,025%.
The closest foreign analogues of steel 15H1M1 °F are in Europe and Germany — steel 15CrMoV5−9, which is smelted according to DIN 17211, USA steel 1.8521. In accordance with EN 10204 these analogues have the following composition:
|The percentage||0,130 0,18…||To 0.40||0,8…1,1||1,2…1,5||0,8…1,1||0,2…0,3|
Steel 15CrMoV5−9, 1.8521 characterized by less tolerance for sulphur and phosphorus, which should not be above 0.030 and 0.025%. Also allowed a certain amount of free nitrogen (not more than 0,006%).
Buy high-temperature structural steel grades 15H1M1 °F, 15CrMoV5−9, 1.8521 at prices from the manufacturer, the company offers Electrocentury-steel. The provider ensures timely delivery of the purchased products and the quality of the sheet, ribbon and wire.
Considered steel can be subjected to various types of heat treatment chastnotsi in the high temperature carburizing, after which the metal acquires a higher surface hardness simultaneously with a viscous core. After annealing to rent has the following mechanical properties — tensile strength up to 1100 MPa, tensile ductility up to 750 MPa, elongation up to 10…12% and a hardness 248 HB.
These have become widely used in the manufacture of ships, various vehicles, infrastructure objects (bridges, viaducts, overpasses), as well as in the manufacture of vessels operated under increased pressure.
Supplier company Electrocentury-steel offers to buy a sheet, tape and wire of low-alloy structural steel grades 15H1M1 °F, 15CrMoV5−9, 1.8521. Price from the manufacturer. Buy steel can be delivery to any place which stipulates the buyer.