Aluminium AD0 (1011)

Designation

Name The value
Designation GOST Cyrillic АД0
Designation GOST Latin AD0
Transliteration AD0
By chemical elements -
Name The value
Designation GOST Cyrillic 1011
Designation GOST Latin 1011
Transliteration 1011
By chemical elements 1011

Description

Aluminium AD0 is used: for the manufacture of flat ingots, cast by semi-continuous method or continuous casting, and is intended for rolling into sheets, strips and other semi-finished products (strips, plates, profiles, panels, rods, tubes, drawn wire, stampings and forgings) by hot or cold deformation, as well as ingots and slabs; the profiles pressed extra virgin for the manufacture of radiators of cooling of semiconductor devices; extruded pipes with controlled inner diameter from 14 to 42 mm for heat exchangers; compressed large pipes; Polutov and profiles for cold end; foil used for the manufacture of condensers; heat exchangers evaporators and condensers with two-sided bulge of the channel used in domestic refrigerators and freezers; roll foil used for thermal, hydro and sound insulation; cold-rolled foil intended for packaging of food, drugs, medical devices, cosmetic products industry, as well as for the production of packaging materials based on it.

Note

ISO 209−1 aluminum brand AD0 is designated А199,5 and 1050А, aluminum brand AD0E (with guaranteed electrical characteristics) is designated ЕА199,5 and 1350.

Standards

Name Code Standards
Tape В54 GOST 1018-77, GOST 13726-97, TU 1-2-133-77, TU 1-2-421-81, TU 1-2-432-82, TU 1-2-433-82, TU 1-2-434-82
Tubes of non-ferrous metals and alloys В64 GOST 18475-82, GOST 18482-79, OST 1 92048-90, OST 1 92048-76, OST 1 92047-76, TU 1-3-041-91, TU 1-3-118-91, TU 1-3-138-91, TU 1-5-027-77, TU 1-3-67-90, TU 1-3-094-93, TU 1-3-67-98
Bars В55 GOST 21488-97, TU 1-2-253-78
Non-ferrous metals, including rare, and their alloys В51 GOST 4784-97, GOST 9498-79, GOST 19437-81, TU 1-1-166-79, TU 1-4-119-81, TU 1-4-162-80, TU 1-4-242-89
Sheets and strips В53 GOST 618-73, GOST 17232-99, GOST 21631-76, GOST 25001-81, GOST 25905-83, GOST 745-2003, TU 1-9-1048-87
Bars and shapes В52 GOST 8617-81, GOST 13616-97, GOST 13617-97, GOST 13618-97, GOST 13619-97, GOST 13620-90, GOST 13621-90, GOST 13622-91, GOST 13623-90, GOST 13624-90, GOST 13737-90, GOST 13738-91, GOST 17575-90, GOST 17576-97, GOST 29296-92, GOST 29303-92, GOST Р 50066-92, GOST Р 50067-92, GOST Р 50077-92, OST 1 92093-83, TU 1-2-368-77, TU 1-9-631-73
Wire from nonferrous metals and their alloys В74 OST 1 92005-2002
Processing of metals by pressure. Forgings В03 OST 26-01-152-82

Chemical composition

Standard Mn Si Fe Cu Al Ti Zn Mg
GOST 4784-97 ≤0.05 ≤0.25 ≤0.4 ≤0.05 ≥99.5 ≤0.05 ≤0.07 ≤0.05
Al is the base.
According to GOST 4784-97, the mass fraction of other impurities is ≤ 0.03% of each, the total mass fraction of all impurities is ≤ 0.50%. In AD0 grade aluminum for sheet blanks subjected to further forming, titanium can be introduced up to 0.15%. For aluminum ADOE (with guaranteed electrical characteristics), the mass percentages of impurities are set: silicon ≤ 0.10%, copper ≤ 0.050%, manganese ≤ 0.010%, chromium ≤ 0.010%, iron ≤ 0.40%, zinc ≤ 0.050%, boron ≤ 0.050, titanium + vanadium ≤ 0.020%, the amount of other impurities (not regulated) ≤ 0.10%.

Mechanical properties

Section, mm sT|s0,2, MPa σU, MPa d5, % d d10
The tape is supplied according to GOST 1018-77 (samples)
0.3-0.7 - ≥70 - ≥20 -
0.3 - 100-150 - ≥2.5 -
0.35-0.7 - 120-150 - ≥3 -
Sheet metal in delivery condition according to GOST 21631-76, OST 4.021.047-92 tape according to GOST 13726-97 (samples transverse)
5-10.5 - ≥70 - ≥15 -
0.3-0.5 - ≥60 - ≥20 -
0.5-0.9 - ≥60 - ≥25 -
0.9-10.5 - ≥60 - ≥30 -
0.3-0.8 - ≥145 - ≥3 -
0.8-3.5 - ≥145 - ≥4 -
3.5-10.5 - ≥130 - ≥5 -
0.8-4.5 - ≥100 - ≥6 -
Plates according to GOST 17232-99 in the delivery condition (transverse specimens)
11-25 - ≥78 ≥18 - -
25-80 - ≥64 ≥15 - -
Forging after annealing at OST 26-01-152-82
≥30 ≥60 ≥25 - -
The wire drawn according to OST 1 92005-2002
≤12 - - - ≥20 -
Extruded normal strength according to GOST 8617-81 on delivery
- ≥59 ≥20 - -
The pressed bars normal strength in the delivery condition according to GOST 21488-97 (longitudinal samples)
8-300 - ≥60 ≥25 - -
Extruded aluminum tubes with internal diameter control for heat exchangers as supplied without a heat treatment on the other 1-3-67-90 (in the section you specify an internal pipe diameter)
14-42 - 59-98 - ≥28 -
Tubes extruded in the state of delivery according to GOST 18482-79 (samples, in cross-section shows the thickness of the wall)
- ≥60 ≥20 - -
Large-size extruded tubes according to OST 1 92048-76 on delivery
- ≥59 ≥20 - -
Cold-rolled tubes in the delivery condition according to GOST 18475-82, OST 4.021.119-92 samples (in cross-section shows the thickness of the wall)
- ≥60 - - ≥20
≤2 - ≥80 - - ≥4
2-5 - ≥80 - - ≥5

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d5 Elongation after rupture
d Elongation after rupture
d10 Elongation after rupture

Physical characteristics

Temperature Е, HPa r, kg/m3 l, W/(m · °C) R, Mr. · m a, 10-6 1/°C
20 71 2710 - 292 -
100 - - 226 - 24
200 - - - - 256

A description of the physical symbols

Name Description
Е The normal elasticity modulus
r Density
l Coefficient of thermal conductivity
R UD. the resistivity
С Specific heat