Alloy AM5 (АЛ19)

Designation

Name	The value
Designation GOST Cyrillic	АМ5
Designation GOST Latin	AM5
Transliteration	AM5
By chemical elements	-

Name	The value
Designation GOST Cyrillic	АЛ19
Designation GOST Latin	AL19
Transliteration	AL19
By chemical elements	-

Description

The AM5 alloy used: for the manufacture of ingots; circular ingots intended for remelting and manufacture of high-strength and heat resisting shaped castings with different casting methods (sand casting, investment casting, gravity die casting).

Note

Aluminum foundry of high-strength heat-resistant alloy of the system Al-Cu-Mn.

Standards

Name	Code	Standards
Non-ferrous metals, including rare, and their alloys	В51	GOST 1583-93, OST 1 90377-87, TU 1-83-28-75
Castings, non-ferrous metals and alloys	В84	OST 1 80029-83, OST 1 90180-75

Chemical composition

Standard	Mn	Si	Ni	Fe	Cu	Al	Ti	Zn	Zr	Mg
GOST 1583-93	0.6-1	≤0.3	≤0.1	≤0.2	4.5-5.3	Rest	0.15-0.35	≤0.2	≤0.2	≤0.05
OST 1 90377-87	0.6-0.8	≤0.1	≤0.05	≤0.1	4.5-5.3	Rest	0.25-0.35	≤0.1	≤0.1	≤0.03

Al is the base.
According to GOST 1583-93 is given for the alloy AM5 (AL19). The iron content is indicated for casting in sand molds and for investment models. The iron content during molding in the mold is ≤ 0.30%. The amount of allowable impurities should be for casting in sand molds, for melted models, casting in chill molds ≤ 0.90%.
According to OST 1 90377-87 the chemical composition is given for the alloy grade AL19P. The amount of allowable impurities should not be more than 0.50%. As agreed with the consumer, the content of titanium in the AL19P alloy is within the range of 0.20-0.35%. For the production of the alloy should be used aluminum grade A99.

Mechanical properties

Section, mm	σ_U, MPa	d	HB, MPa
Casting (in land, investment casting, gravity die casting). Mode T4: two-stage heating: 525-535 °C (aging 5-9 h) + 542-548 °C (aging 5-9 hours), quenching in water
	≥294	≥8	≥70
Casting (in land, investment casting, gravity die casting). Mode T5: two-stage heating: 525-535 °C (aging 5-9 h) + 542-548 °C (aging 5-9 hours), quenching in water + incomplete artificial aging at 170-180 °C (exposure 3-6 h)
	≥333	≥4	≥90
Casting into the ground. Mode T7: two-stage heating: 525-535 °C (aging 5-9 h), 542-550 °C (aging 5-9 hours), quenching in water with a temperature of 80-100 °C+ stabilizing vacation at 240-260 °C (extract 3-10 h)
	≥314	≥2	≥80

Description mechanical marks

Name	Description
σ_U	Limit short-term strength
d	Elongation after rupture
HB	Brinell hardness number

Physical characteristics

Temperature	Е, HPa	r, kg/m³	R, Mr. · m
20	70	2780	595

A description of the physical symbols

Name	Description
Е	The normal elasticity modulus
l	Coefficient of thermal conductivity
С	Specific heat