Alloy Amg1 (1510)

Designation

Name The value
Designation GOST Cyrillic АМг1
Designation GOST Latin AMg1
Transliteration AMg1
By chemical elements -
Name The value
Designation GOST Cyrillic 1510
Designation GOST Latin 1510
Transliteration 1510
By chemical elements 1510

Description

Alloy Amg1 is used: for the manufacture of semi-finished products (sheets, tapes, strips, plates, profiles, panels, pipes, wire, stampings and forgings) by hot or cold deformation of welded and riveted structural elements of aircraft construction and shipbuilding, experiencing a relatively light load and require high corrosion resistance.

Note

The high quality alloy system Al-Mg.
ISO 209−1 alloy brand Amg1 has designations and AlMg1 5005.

Standards

Name Code Standards
Tubes of non-ferrous metals and alloys В64 GOST 18475-82, OST 1 92047-76, TU 1-8-084-89
Non-ferrous metals, including rare, and their alloys В51 GOST 4784-97, OST 1 92014-90
Bars and shapes В52 OST 1 92093-83
Bars В55 TU 1-3-016-90

Chemical composition

Standard Mn Cr Si Fe Cu Al Zn Mg
OST 1 92014-90 ≤0.2 - ≤0.1 ≤0.1 ≤0.1 Rest - 0.7-1.6
GOST 4784-97 ≤0.2 ≤0.1 ≤0.3 ≤0.7 ≤0.2 Rest ≤0.25 0.5-1.1
Al is the base.
According to GOST 4784-97, the chemical composition is given for the AMg1 alloy. Mass fraction of each other impurity (not regulated) ≤ 0.05%, total mass fraction of other impurities ≤ 0.15%.
According to OST 1 92014-90 the chemical composition is given for AMg1 alloy. Mass fraction of each other impurity (not regulated) ≤ 0.05%, total mass fraction of other impurities ≤ 0.10%.

Mechanical properties

Section, mm σU, MPa d10
Cold-rolled tubes in the delivery condition according to GOST 18475-82, OST 4.021.119-92 samples (in cross-section shows the thickness of the wall)
120-175 ≥10
≥165 -

Description mechanical marks

Name Description
σU Limit short-term strength
d10 Elongation after rupture

Physical characteristics

Temperature r, kg/m3
20 2690

A description of the physical symbols

Name Description
Е The normal elasticity modulus
l Coefficient of thermal conductivity

Technological properties

Name The value
Weldability The alloy is well welded all types of welding - TIG, contact, spot, and seam welding. The corrosion resistance of the alloy (and the weld) high, is almost the same as that of pure aluminum.
Machinability The poor machinability in the annealed condition and satisfactory cold-worked.
Pressure treatment Well-deformed in hot and cold condition.
Corrosion resistance Alloy with excellent General corrosion resistance, not cloned to stress corrosion cracking and intergranular corrosion (especially in the annealed condition). For additional protection parts against corrosion is anodizing or applied coatings.
Soldering Alloy satisfactorily soldered.