Steel 015Х18Н15Р13 (ЭП166Б)

Designation

Name The value
Designation GOST Cyrillic 015Х18Н15Р13
Designation GOST Latin 015X18H15P13
Transliteration 015H18N15R13
By chemical elements 015Cr18Н15B13
Name The value
Designation GOST Cyrillic ЭП166Б
Designation GOST Latin EP166B
Transliteration EhP166B
By chemical elements -

Description

015Х18Н15Р13 steel is used: for the manufacture of pipes used in chemical engineering.

Note

Hromonikelevoj corrosion and heat resistant steel, alloyed by boron.

Standards

Name Code Standards
Blanks. Of the workpiece. Slabs В31 TU 14-1-2816-79

Chemical composition

Standard C S P Mn Cr Si Ni Fe B Nb
TU 14-1-2816-79 ≤0.015 ≤0.02 ≤0.02 0.6-1.1 17-19 ≤0.6 14-16 Rest ≤0.13 0.1-0.4
Fe is the basis.
According to TU 14-1-2816-79, the chemical composition is given for steel grade 015X18H15P13-VD; EP166B-VD. In the finished metal, the aluminum content is not more than 0.30%, nitrogen is not more than 0.050%. In the finished metal, the content of cobalt is controlled, the results of the control are not a defective feature, but are indicated in the certificate. By agreement of the parties, the pipe billet is supplied with a cobalt content of not more than 0.0050%. In the finished metal, if the requirements of TU are complied with, the deviation by the content of carbon + 0.0050%, the boron content ± 0.040% is permissible.

Mechanical properties

Section, mm sT|s0,2, MPa σU, MPa d5, %
Tubular billet on the other 14-1-2816-79. Quenching in water from 950-970 °C
≥175 ≥470 ≥38
≥127 ≥320 ≥27

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d5 Elongation after rupture