Steel 09G2D

Designation

Name The value
Designation GOST Cyrillic 09Г2Д
Designation GOST Latin 09G2D
Transliteration 09G2D
By chemical elements 09Mn2Cu

Description

Steel 09G2D used: for the manufacture of farm stands, components of the upper trim cars, spinal beams, I-beams and other parts and hardware in the building.

Note

Steel low alloy manganese with copper. The degree of deoxidation — SP.

Standards

Name Code Standards
Classification, nomenclature and General rules В20 GOST 19281-89
Steel pipes and fittings to them В62 GOST 20295-85, GOST 24950-81
Bars and shapes В22 GOST 5267.0-90, GOST 8278-83, GOST 8281-80, GOST 8282-83, GOST 8283-93, GOST 9234-74, GOST 10551-75, GOST 11474-76
Sheets and strips В23 GOST 82-70, GOST 17066-94, GOST 19282-73, TU 14-1-3023-80, TU 14-1-4632-93
Sheets and strips В33 TU 14-1-4431-88
Bars and shapes В32 TU 14-136-367-2008

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu N As Al Ti
GOST 17066-94 ≤0.12 ≤0.04 ≤0.035 ≤1.4 ≤0.3 0.17-0.37 ≤0.3 Rest 0.15-0.3 ≤0.008 ≤0.08 ≤0.03 ≤0.03
GOST 19282-73 ≤0.12 ≤0.04 ≤0.035 1.4-1.8 ≤0.3 0.17-0.37 ≤0.3 Rest 0.15-0.3 ≤0.008 ≤0.08 ≤0.05 ≤0.03
Fe is the basis.
According to GOST 17066-94, the mass fraction of arsenic is allowed up to 0.015%, with the mass fraction of phosphorus being not more than 0.030%.
According to GOST 19282-73, it is allowed to modify steel with calcium and rare-earth elements from the calculation of the introduction of not more than 0.02% calcium and 0.05% rare-earth elements into the metal.
According to GOST 19281-89 and GOST 19282-73, it is allowed to add aluminum and titanium from the calculation of the mass fraction in the rolled aluminum - no more than 0.050%, titanium - no more than 0.030%.

Mechanical properties

Section, mm sT|s0,2, MPa σU, MPa d5, % d4
Pre-painted steel sheet of high-strength steel in the delivery state GOST 17066-94
0.5-3.9 ≥295 ≥440 - ≥20
The plates and universal broadband in the state of delivery GOST 19282-73
≤20 ≥305 ≥440 ≥21 -
Pre-painted steel sheet of high-strength steel in the delivery state GOST 17066-94
0.5-2 ≥265 ≥390 - ≥17
The plates and universal broadband in the state of delivery GOST 19282-73
20-32 ≥295 ≥440 ≥21 -
Pre-painted steel sheet of high-strength steel in the delivery state GOST 17066-94
2.1-3.9 ≥295 ≥410 - ≥20

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d5 Elongation after rupture
d4 Elongation after rupture

Technological properties

Name The value
Weldability without restrictions