    • Designation

    Name The value
    Designation GOST Cyrillic 4ХВ2С
    Designation GOST Latin 4XB2C
    Transliteration 4HV2S
    By chemical elements 4CrW2С

    Description

    4ХВ2С steel is used: for the production of pneumatic tools: chisels, swages, punches and trimming dies complex forms, working with high impact loads.

    Standards

    Name Code Standards
    Bars and shapes В22 GOST 1133-71, GOST 2590-2006
    Sheets and strips В33 GOST 4405-75
    Bars and shapes В32 GOST 7417-75, GOST 8559-75, GOST 8560-78, GOST 14955-77, TU 14-11-245-88
    Blanks. Of the workpiece. Slabs В31 OST 24.952.01-89

    Chemical composition

    Standard C S P Mn Cr Si Ni Cu W
    0.35-0.45 ≤0.03 ≤0.03 0.15-0.4 1-1.3 0.6-0.9 ≤0.35 ≤0.3 2-2.5

    Mechanical properties

    t отпуска, °C sT|s0,2, MPa σU, MPa d5, % y, % KCU, kJ/m2 HRC
    Quenching in oil at 880 °C to + Leave (exposure 8 h), air cooling
    200 ≥1700 ≥1910 ≥5 ≥35 ≥230 ≥55
    Quenching in oil at 880 °C to + Leave at 430 °C (exposure 2 hours), air cooling
    - ≥1300 ≥1470 ≥8 ≥35 ≥290 -
    Quenching in oil at 880 °C to + Leave (exposure 8 h), air cooling
    300 ≥1630 ≥1760 ≥8 ≥36 ≥220 ≥52
    Quenching in oil at 880 °C to + Leave at 430 °C (exposure 2 hours), air cooling
    - ≥1320 ≥1500 ≥10 ≥47 ≥440 -
    Quenching in oil at 880 °C to + Leave (exposure 8 h), air cooling
    400 ≥1450 ≥1620 ≥9 ≥37 ≥290 ≥50
    Quenching in oil at 880 °C to + Leave at 430 °C (exposure 2 hours), air cooling
    - ≥1340 ≥1520 ≥12 ≥49 ≥410 -
    Quenching in oil at 880 °C to + Leave (exposure 8 h), air cooling
    500 ≥1260 ≥1370 ≥10 ≥40 ≥340 ≥42
    Quenching in oil at 880 °C to + Leave at 430 °C (exposure 2 hours), air cooling
    - ≥1250 ≥1370 ≥13 ≥60 ≥390 -
    Quenching in oil at 880 °C to + Leave (exposure 8 h), air cooling
    600 ≥1140 ≥1180 ≥11 ≥48 ≥410 ≥39
    Quenching in oil at 880 °C to + Leave at 430 °C (exposure 2 hours), air cooling
    - ≥1090 ≥1170 ≥13 ≥60 ≥420 -
    - ≥590 ≥590 ≥20 ≥80 ≥880 -

    Description mechanical marks

    Name Description
    sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
    σU Limit short-term strength
    d5 Elongation after rupture
    y The relative narrowing
    KCU Toughness
    HRC Rockwell hardness (indenter diamond spheroconical)

    Technological properties

    Name The value
    Weldability Steel is not used for welded structures.
    Склонность к отпускной хрупкости Tend not.
    The temperature of forging Start - 1180 °C, the end - 850 °C slow Cooling in the wells.
    Flock-sensitive sensitivity Sensitive.