Steel 10Х13Г12БС2Н2Д2 (ДИ59)
|Designation GOST Cyrillic||10Х13Г12БС2Н2Д2|
|Designation GOST Latin||10X13G12BC2H2D2|
|By chemical elements||10Cr13Mn12NbС2Н2Cu2|
|Designation GOST Cyrillic||ДИ59|
|Designation GOST Latin||DI59|
|By chemical elements||CuИ59|
10Х13Г12БС2Н2Д2 steel is used: for the manufacture of seamless cold, warm, hot-wrought, including hot-pressed and hot-pressed reduced pipes for steam boilers and pipelines, installations with high and supercritical steam parameters.
Bromomalonate austenitic steel.
|Blanks. Of the workpiece. Slabs||В31||TU 14-1-2870-80|
|Steel pipes and fittings to them||В62||TU 14-3Р-55-2001|
According to TU 14-3R-55-2001, a technological addition of rare earth elements is possible to improve the quality of the metal. The content of residual elements is according to GOST 5632. Zirconium is introduced into steel to 0.10%, cerium to 0.080%, titanium to 0.10%, boron up to 0.0030%, and chemical analysis is not determined. The presence of up to 0.25% aluminum in steel is allowed.
|Section, mm||sT|s0,2, MPa||σU, MPa||d5, %||y, %|
|Seamless pipes for steam boilers and pipelines according to TU 14-3P-55-2001. Austenization at 1060-1080 °C, air cooling|
Description mechanical marks
|sT|s0,2||Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%|
|σU||Limit short-term strength|
|d5||Elongation after rupture|
|y||The relative narrowing|