Designation
| Name |
The value |
| Designation GOST Cyrillic |
06Х15Н6МВФБ |
| Designation GOST Latin |
06X15H6MBFB |
| Transliteration |
06H15N6MVFB |
| By chemical elements |
06Cr15Н6MoWVNb |
| Name |
The value |
| Designation GOST Cyrillic |
ВНС16 |
| Designation GOST Latin |
BHC16 |
| Transliteration |
VNS16 |
| By chemical elements |
WНС16 |
Description
06Х15Н6МВФБ steel is used: for the manufacture of wear-resistant corrosion-resistant and heat-resistant parts and units of equipment chemical and power engineering.
Standards
| Name |
Code |
Standards |
| Blanks. Of the workpiece. Slabs |
В31 |
TU 14-1-1214-75, TU 14-1-2903-80 |
| Processing of metals by pressure. Forgings |
В03 |
TU 14-1-1444-75 |
| Bars and shapes |
В32 |
TU 14-1-2229-77 |
| Sheets and strips |
В33 |
TU 14-1-2615-79, TU 14-1-2624-79, TU 14-1-3405-82, TU 14-1-3411-82 |
| Steel pipes and fittings to them |
В62 |
TU 14-159-186-89 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Cu |
V |
Mo |
Nb |
W |
| TU 14-159-186-89 |
0.05-0.08 |
≤0.015 |
≤0.025 |
≤0.6 |
13.5-15 |
≤0.6 |
5.2-5.7 |
Rest |
≤0.3 |
0.15-0.25 |
0.8-1 |
0.08-0.15 |
0.7-1 |
Fe is the basis.
According to TU 14-159-186-89, According to TU 14-1-2903-80 the chemical composition is presented for steel grade 06H15N6MVFB-SH (VNS16-Sh). Deviations in chemical composition are allowed: carbon +0.010%, nickel ± 0.010%, silicon +0.10%, manganese +0.10%, molybdenum ± 0.10%, chromium ± 0.10%, for tungsten ± 0.10%, for niobium + 0.010 / -0.020%, for vanadium + 0.010 / -0.020%.
For limited use, the content of residual elements should not exceed: copper - 0.20%, titanium - 0.050%. The content of the residual elements can not be determined. The steel is marked 06Х15Н6МВФБУ-Ш (ВНС16У-Ш).
Mechanical properties
| Section, mm |
sT|s0,2, MPa |
σU, MPa |
d5, % |
| Tubular billet on the other 14-1-2903-80. Quenching in air from 1,000 °C±10 ° C + Vacation at 490±15 °With (extract of 1.5-3.0 hours) (samples with allowance for grinding) |
|
≥980 |
≥1180 |
≥12 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d5 |
Elongation after rupture |
Technological properties
| Name |
The value |
| Macrostructure and pollution |
The macrostructure of the workpiece on the other 14-1-2903-80 when checking for cross etched templeto should not have shrinkage, blistering, delamination, foreign metal and slag inclusions are visible without using the magnifying devices. Allowable defects of the macrostructure shall not exceed, in points: Central porosity ≤ 1,0; - point nonuniformity ≤ 1,0; - exudation square ≤ 1,0; - layer-by-layer crystallization and the light circuit ≤ 3,0. Pollution steel non-metallic inclusions in points: - oxides of stroke (OS) ≤ 2,0; - oxides of point () ≤ 2,0; - silicates fragile (CX) ≤ 1,0; - silicates plastic (SP) ≤ 1,0; - silicates, non-deformed (SN) ≤ 2,5; sulphides (S) ≤ 1,0; - nitrides stroke (NS) ≤ 1,0; the nitrides of the point (NT) ≤ 1,0. |
| Particularities of production of goods |
On the other 14-1-2903-80 billet is supplied in the annealed or tempered condition, stripped in accordance with the agreed standard. Clan or extract ratio of the workpiece must be not less than 4.5. |