Steel 15ХМФА (15ХМФ)

Designation

Name The value
Designation GOST Cyrillic 15ХМФА
Designation GOST Latin 15XMFA
Transliteration 15HMFA
By chemical elements 15CrMoV
Name The value
Designation GOST Cyrillic 15ХМФ
Designation GOST Latin 15XMF
Transliteration 15HMF
By chemical elements 15CrMoV

Description

15ХМФА steel is used: for the manufacture of seamless hot-deformed pipes with improved corrosion and cold-resistance (article 15ХМФА), with an outer diameter from 60 to 426 mm, strength class not less than K54, infield pipelines, transporting products of oil wells (high-pressure conduits at a pressure of 24.0 MPa).

Note

Structural alloy steel of high corrosion resistance and cold-resistance.

Standards

Name Code Standards
Steel pipes and fittings to them В62 TU 1317-006.1-593377520-2003

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu N Al V Mo
TU 1317-006.1-593377520-2003 0.13-0.17 ≤0.01 ≤0.015 0.45-0.65 0.5-0.7 0.17-0.37 ≤0.2 Rest ≤0.2 ≤0.008 0.02-0.05 0.04-0.09 0.1-0.15
Fe is the basis.
According to TU 1317-006.1-593377520-2003 the chemical composition is given for steel grade 15ХМФА. The mass fraction of hydrogen in the steel in the metal of the pipe should not exceed 1.0 ppm (2.0 ppm in the ladle sample, niobium and titanium can be added from the calculation of the mass fraction to 0.030% and 0.010%, respectively.) In the deoxidized steel for the globularization of sulfide inclusions enter calcium (silicocalcium) or cerium from the calculation of the mass fraction of 0.050%.

Mechanical properties

Section, mm sT|s0,2, MPa σU, MPa d5, % KCU, kJ/m2 HRB
Seamless tubes gas & oil heat-treated in the delivery condition on the other 1317-006.1-593377520-2003 (samples in the delivery condition specified strength class, in the column the value is KCU KCV-50 °C)
60-426 383-510 ≥530 ≥23 ≥980 ≤92

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d5 Elongation after rupture
KCU Toughness
HRB Rockwell hardness (indenter steel, spherical)

Technological properties

Name The value
Corrosion resistance In the medium H2S: speed General corrosion ≤ 0.3 mm/year; resistance to hydrogen cracking in the CLR ≤ 1 % CTR ≤ 2 %; resistance to sulfide corrosion cracking with voltage ≥ 75 % of σ0,2.