Steel 16ХН3МА

Designation

Name The value
Designation GOST Cyrillic 16ХН3МА
Designation GOST Latin 16XH3MA
Transliteration 16HN3MA
By chemical elements 16CrН3Mo

Description

16ХН3МА steel is used: for the production of hot rolled bars used for the manufacture of paws and cutter drill bits all sizes with air purge, as well as bits from 151 mm and less, borgonovo by hot forming.

Standards

Name Code Standards
Bars and shapes В22 GOST 2590-2006
Bars and shapes В32 TU 3-26-79, TU 3-27-79, TU 3-850-80, TU 3-938-79, TU 14-1-4612-89

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu Mo O
TU 3-850-80 0.13-0.18 ≤0.015 ≤0.02 0.35-0.65 0.4-0.7 0.17-0.37 2.75-3.15 Rest ≤0.3 0.2-0.3 -
TU 3-938-79 0.13-0.17 ≤0.02 ≤0.02 0.3-0.6 0.4-0.7 0.17-0.37 2.85-3.25 Rest ≤0.2 0.25-0.35 -
TU 14-1-4612-89 0.13-0.18 ≤0.015 ≤0.02 0.35-0.65 0.4-0.7 0.17-0.37 2.75-3.15 Rest ≤0.25 0.2-0.3 ≤0.006
Fe is the basis.
According to TU 3-938-79, the chemical composition is given for steel grade 16ХН3МА-Ш.
TU 14-1-4612-89 chemical composition is given for steel grade 16HN3MA-III. Allowable deviations in the chemical composition in the finished rolled product and the mass fraction of residual tungsten, molybdenum, titanium and vanadium - according to GOST 4543.
According to TU 3-850-80 the chemical composition is given for steel grade 16HN3MA. The presence of residual titanium in the steel to 0.030%, tungsten to 0.20% and vanadium to 0.050% is not a defect.

Mechanical properties

Section, mm sT|s0,2, MPa σU, MPa d5, % y, % KCU, kJ/m2 HB, MPa
Bars hot rolled as supplied on the other 14-1-4612-89. 1-I'm quenching in oil with 880-900 °C + 2 quenching in oil from 800-820 °C + Vacation at 170-220 °C, air cooling (longitudinal samples)
25 ≥835 ≥930 ≥10 ≥50 ≥1080 ≤269
Bars hot rolled as supplied on the other 3-850-80. 1-I'm quenching in oil from 890±15 °C + 2 quenching in oil from 775±15 °C + Vacation at 170-220 °C, air cooling (longitudinal samples)
≥833 ≥931 ≥10 ≥50 ≥980 -

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d5 Elongation after rupture
y The relative narrowing
KCU Toughness
HB Brinell hardness number

Physical characteristics

Temperature r, kg/m3 a, 10-6 1/°C
1470 7280 89
1506 6990 82

A description of the physical symbols

Name Description
Е The normal elasticity modulus
r Density
l Coefficient of thermal conductivity
R UD. the resistivity

Technological properties

Name The value
Macrostructure and pollution Macrostructure of steel ready rods on the other 3-850-80 checked for breaks and pickled Templeton, must meet the requirements of GOST 4543 and should not have shrinkage, porosity, bubbles, cracks, delamination, inclusions and placenow. Upon detection placenow steel is rejected. Evaluation of the macrostructure of the etched on Templeton is on scales GOST 10243. Permitted: Central porosity; a point inhomogeneity; phase separation squared, General, regional and Pousada liquation not more than 2 points; layer-by-layer crystallization and the light circuit is not more than 3 points. Not allowed subcortical bubbles and intergranular cracks. Steel is controlled on the contamination of non-metallic inclusions, the content of which is determined according to GOST 1778 for 6 samples and should not exceed the contents in points (average/maximum): - FROM Point - 2,0/4,0; - Stroke OS - 3,0/4,0; - Fragile CX - 3,5/4,0; Plastic SP 2,5/4,0; - non-deformable SN - 2,5/4,0; - Sulfides C - 2,5/4,0; Nitrides N - 1,5/2,5.
Microstructure The austenitic grain size shall be not larger than the number 5 according to GOST 5639.
Particularities of production of goods Bars hot rolled on the other 3-850-80 are supplied in heat-treated (annealed or vysokoopasnye) with hardness not exceeding 269 HB (indentation diameter not less than 3.7 mm). Hardenability of steel (after normalization at 920±10 °C or quenching from 890±10 °C) - Hardness HRC should be at a distance of 4.5 mm from the end 36,5÷42,5, and at a distance of 30 mm from the end - 23÷33.